PSL Spheres 1 micron to 160 microns, NIST Traceable, Particle Size Standards
PSL Spheres are excellent for use with any application that requires calibration of a size response curve using NIST traceable, size standards with narrow standard deviation of the size peak. The mean size diameter of these PSL spheres are calibrated with NIST traceable microscopy methods. The size distribution and uniformity are measured by electrical resistance analysis or optical microscopy. Polystyrene latex spheres range from 1 µm to 160 µm and are made from polystyrene (PSL). PSL Spheres are used instead of irregularly shaped particles to minimize the laser response of analytical instruments that are sensitive to particle shape. Products from 1 to 160 µm are packaged as aqueous suspensions in 15 mL dropper-tipped bottles. Concentration is maintained at 1.05 grams per cm cubed. Each bottle of PSL spheres contains a Certificate of Calibration and Traceability to NIST which includes a description of the calibration method and its uncertainty, and a table of chemical and physical properties. A Material Safety Data Sheet (MSDS) with handling and disposal instructions is also available. Packages are lot-numbered for convenient technical service and support after the sale.
PSL Spheres | 1 µm to 160 µm |
Particle Composition | Polystyrene Latex, PSL Spheres |
Particle Density | 1.05 g/cm³ |
Index of Refraction | 1.59 @ 589nm (25°C) |
Bottle Size | 15 mL |
Expiration Date | ≤ 24 months |
Additives | Contains trace amount surfactant to reduce agglomeration |
Suggested Storage Temp. | 2-8°C |
Bottle Size and Volume | 15ml (A) Bottle |
PSL Spheres, 1um to 160um, Polystyrene Latex Spheres | ||||
Product Part # |
Nominal Diameter |
Certified Mean Peak |
Size Distribution, S & CV |
Solids Concentration (%) in 15ml Liquid Volume |
AP4009A |
0.994 μm |
0.994 μm ± 0.021 μm |
0.010 μm (1.0%) |
1.00% |
AP4010A |
1.0 μm |
1.019 μm ± 0.015 μm |
0.010 μm (1.0%) |
1.00% |
AP4011A |
1.1 μm |
1.101 μm ± 0.017 μm |
0.012 μm (1.1%) |
1.00% |
AP4013A |
1.3 μm |
1.361 μm ± 0.015 μm |
0.021 μm (1.5%) |
1.00% |
AP4016A |
1.6 μm |
1.587 μm ± 0.018 μm |
0.021 μm (1.3%) |
1.00% |
AP4018A |
1.8 μm |
1.745 μm ± 0.022 μm |
0.019 μm (1.1%) |
1.00% |
AP4202A |
2.0 μm |
1.999 μm ± 0.020 μm |
0.022 μm (1.1%) |
1.00% |
AP4025A |
2.5 μm |
2.504 μm ± 0.027 μm |
0.025 μm (1.0%) |
0.50% |
AP4203A |
3.0 μm |
3.002 μm ± 0.019 μm |
0.029 μm (1.1%) |
0.50% |
AP4204A |
4.0 μm |
4.000 μm ± 0.043 μm |
0.04 μm (1.0%) |
0.40% |
AP4205A |
5.0 μm |
4.993 μm ± 0.040 μm |
0.05 μm (1.0%) |
0.30% |
AP4206A |
6.0 μm |
6.007 μm ± 0.040 μm |
0.06 μm (1.0%) |
0.30% |
AP4207A |
7.0 μm |
6.982 μm ± 0.045 μm |
0.07 μm (1.0%) |
0.30% |
AP4208A |
8.0 μm |
7.979 μm ± 0.075 μm |
0.09 μm (1.1%) |
0.30% |
AP4209A |
9.0 μm |
8.956 μm ± 0.082 μm |
0.09 μm (1.0%) |
0.30% |
AP4210A |
10 μm |
10.00 μm ± 0.08 μm |
0.09 μm (0.9%) |
0.20% |
AP4212A |
12 μm |
12.01 μm ± 0.11 μm |
0.12 μm (1.0%) |
0.20% |
AP4215A |
15 μm |
14.97 μm ± 0.10 μm |
0.13 μm (0.90%) |
0.30% |
AP4220A |
20 μm |
19.99 μm ± 0.25 μm |
0.28 μm (1.4%) |
0.30% |
AP4225A |
25 µm |
24.61 µm ± 0.22 µm |
0.27 µm (1.1%) |
0.40% |
AP4230A |
30 μm |
29.75 μm ± 0.56 μm |
0.42 μm (1.4%) |
0.60% |
AP4240A |
40 μm |
39.94 μm ±0.35 μm |
0.52 μm (1.3%) |
0.70% |
AP4250A |
50 μm |
50.2 μm ± 0.30 μm |
0.5 μm (1.0%) |
1.40% |
AP4260A |
60 μm |
59.2 μm ± 0.6 μm |
0.8 μm (1.4%) |
1.20% |
AP4270A |
70 μm |
69.1 μm ± 0.9 μm |
0.8 μm (1.2%) |
2.0% |
AP4280A |
80 μm |
79.4 μm ± 0.5 μm |
1.0 μm (1.3%) |
1.80% |
AP4310A |
100 μm |
100 μm ± 1.5 μm |
1.6 μm (1.6%) |
2.10% |
AP4311A |
113 μm |
113 μm ± 1.0 μm |
1.6 μm (1.4%) |
2.60% |
AP4314A |
140 μm |
138 μm ± 2.0 μm |
2.2 μm (1.6%) |
4.00% |
AP4316A |
160 µm |
161 µm ± 3.1 µm |
2.9 µm (1.8%) |
4.80% |